| 銘柄(description) | 旭#78 | 旭#80 | 旭#70 | 旭#70L | 旭F-200 | 旭#66 | 旭#65 |
|---|---|---|---|---|---|---|---|
| 試験項目(test items) | |||||||
| ムーニー粘度 (mooney viscosity) '@125℃ ML1+4' |
56.2 | 47.5 | 48.3 | 48.2 | 56.1 | 40.4 | 42.5 |
| ムーニースコーチ (mooney scorch) '@125℃ t5 |
8.8 | 13.8 | 10.0 | 10.1 | 13.9 | 20.3 | 15.2 |
| 硬さ (hardness) (JIS) |
59 | 56 | 56 | 53 | 61 | 56 | 54 |
| 300%モジュラス(MPa) (300%modulus) |
10.3 | 7.6 | 9.7 | 6.6 | 12.3 | 9.6 | 9.4 |
| 引張強さ(MPa) (tensile strength) |
24.1 | 23.4 | 23.1 | 22.8 | 16.2 | 18.7 | 18.4 |
| 伸び(%) (ultimate elongation) |
550 | 631 | 584 | 641 | 419 | 599 | 587 |
| 反発弾性(%) (rebound resilience) |
37.3 | 37.9 | 41.0 | 41.0 | 47.5 | 51.2 | 50.7 |
| 銘柄(description) | 旭#60HN | 旭#60H | 旭#60U | 旭#60 | 旭#55 | 旭#50HG | 旭#52 |
|---|---|---|---|---|---|---|---|
| 試験項目(test items) | |||||||
| ムーニー粘度 (mooney viscosity) '@125℃ ML1+4' |
44.1 | 41.4 | 38.6 | 43.4 | 38.0 | 38.7 | 39.7 |
| ムーニースコーチ (mooney scorch) '@125℃ t5 |
14.8 | 10.8 | 17.4 | 14.3 | 18.8 | 22.9 | 23.0 |
| 硬さ (hardness) (JIS) |
56 | 56 | 54 | 54 | 50 | 50 | 53 |
| 300%モジュラス(MPa) (300%modulus) |
10.2 | 10.5 | 9.1 | 8.8 | 6.0 | 6.2 | 8.0 |
| 引張強さ(MPa) (tensile strength) |
19.6 | 18.4 | 18.6 | 16.7 | 14.8 | 13.9 | 15.7 |
| 伸び(%) (ultimate elongation) |
581 | 526 | 574 | 556 | 642 | 632 | 595 |
| 反発弾性(%) (rebound resilience) |
48.6 | 48.4 | 51.1 | 52.5 | 56.1 | 57.0 | 55.4 |
| 銘柄(description) | 旭#51 | 旭#50U | 旭#50 | 旭#35 | 旭#15HS | 旭#15 | 旭#8 |
|---|---|---|---|---|---|---|---|
| 試験項目(test items) | |||||||
| ムーニー粘度 (mooney viscosity) '@125℃ ML1+4' |
35.7 | 36.1 | 35.8 | 33.9 | 37.6 | 36.8 | 30.3 |
| ムーニースコーチ (mooney scorch) '@125℃ t5 |
19.5 | 15.2 | 18.5 | 13.6 | 20.7 | 16.6 | 21.8 |
| 硬さ (hardness) (JIS) |
48 | 48 | 48 | 47 | 52 | 47 | 43 |
| 300%モジュラス(MPa) (300%modulus) |
5.5 | 6.1 | 5.5 | 5.4 | 6.9 | 5.2 | 3.3 |
| 引張強さ(MPa) (tensile strength) |
16.2 | 17.6 | 16.8 | 15.5 | 14.3 | 14.3 | 16.3 |
| 伸び(%) (ultimate elongation) |
709 | 667 | 712 | 663 | 617 | 671 | 786 |
| 反発弾性(%) (rebound resilience) |
57.5 | 53.9 | 56.8 | 56.3 | 56.7 | 58.2 | 60.1 |
| 銘柄(description) | アサヒ サーマル |
旭AX-015 | IRB |
|---|---|---|---|
| 試験項目(test items) | |||
| ムーニー粘度 (mooney viscosity) '@125℃ ML1+4' |
36.4 | 39.7 | 45.1 |
| ムーニースコーチ (mooney scorch) '@125℃ t5 |
14.9 | 23.0 | 11.4 |
| 硬さ (hardness) (JIS) |
45 | 53 | 56 |
| 300%モジュラス(MPa) (300%modulus) |
4.0 | 8.0 | 9.6 |
| 引張強さ(MPa) (tensile strength) |
20.0 | 15.7 | 23.3 |
| 伸び(%) (ultimate elongation) |
773 | 595 | 568 |
| 反発弾性(%) (rebound resilience) |
53.3 | 55.4 | 41.7 |
- ※加硫時間は30分です。
- ※但し、アサヒサーマル、旭#15、旭#15HS配合部数は80部です。
SBR配合表
| SBR | 137.5 |
|---|---|
| カーボンブラック | 65 |
| ステアリン酸 | 1 |
| 亜鉛華 | 3 |
| 促進剤DM | 1.5 |
| 促進剤D(DPG) | 0.5 |
| 硫黄 | 1.5 |