| 銘柄(description) | 旭#78 | 旭#80 | 旭#70 | 旭#70L | 旭F-200 | 旭#66 | 旭#65 |
|---|---|---|---|---|---|---|---|
| 試験項目(test items) | |||||||
| ムーニー粘度 (mooney viscosity) '@125℃ ML1+4' |
71 | 63 | 59 | 57 | 58 | 52 | 53 |
| ムーニースコーチ (mooney scorch) '@125℃ t5 |
8.4 | 10.3 | 8.8 | 9.0 | 9.6 | 11.4 | 11.0 |
| 硬さ (hardness) (JIS) |
71 | 68 | 68 | 65 | 67 | 66 | 65 |
| 300%モジュラス(MPa) (300%modulus) |
16.1 | 13.6 | 15.5 | 12.8 | 16.8 | 15.5 | 13.9 |
| 引張強さ(MPa) (tensile strength) |
25.5 | 26.3 | 25.8 | 27.2 | 22.9 | 23.5 | 22.9 |
| 伸び(%) (ultimate elongation) |
438 | 501 | 459 | 521 | 410 | 441 | 459 |
| 反発弾性(%) (rebound resilience) |
49 | 51 | 57 | 58 | 60 | 64 | 64 |
| 銘柄(description) | 旭#60HN | 旭#60H | 旭#60U | 旭#60 | 旭#55 | 旭#50HG | 旭#52 |
|---|---|---|---|---|---|---|---|
| 試験項目(test items) | |||||||
| ムーニー粘度 (mooney viscosity) '@125℃ ML1+4' |
55 | 59 | 53 | 51 | 49 | 51 | 54 |
| ムーニースコーチ (mooney scorch) '@125℃ t5 |
11.5 | 11.4 | 11.4 | 15.8 | 12.1 | 13.7 | 15.5 |
| 硬さ (hardness) (JIS) |
67 | 68 | 64 | 66 | 60 | 62 | 64 |
| 300%モジュラス(MPa) (300%modulus) |
15.5 | 16.8 | 14.9 | 15.7 | 13.3 | 13.9 | 14.6 |
| 引張強さ(MPa) (tensile strength) |
23.7 | 24.7 | 24.2 | 23.4 | 23.1 | 21.1 | 22.5 |
| 伸び(%) (ultimate elongation) |
442 | 438 | 453 | 436 | 469 | 437 | 444 |
| 反発弾性(%) (rebound resilience) |
62 | 63 | 65 | 67 | 69 | 68 | 66 |
| 銘柄(description) | 旭#51 | 旭#50U | 旭#50 | 旭#35 | 旭#15HS | 旭#15 | 旭#8 |
|---|---|---|---|---|---|---|---|
| 試験項目(test items) | |||||||
| ムーニー粘度 (mooney viscosity) '@125℃ ML1+4' |
47 | 49 | 46 | 46 | 57 | 49 | 47 |
| ムーニースコーチ (mooney scorch) '@125℃ t5 |
15.3 | 13.5 | 15.2 | 13.2 | 12.2 | 11.8 | 12.7 |
| 硬さ (hardness) (JIS) |
59 | 59 | 58 | 57 | 71 | 62 | 59 |
| 300%モジュラス(MPa) (300%modulus) |
11.5 | 12.1 | 11.2 | 10.8 | 17.3 | 14.0 | 11.7 |
| 引張強さ(MPa) (tensile strength) |
22.8 | 24.5 | 23.4 | 24.5 | 18.3 | 19.7 | 20.7 |
| 伸び(%) (ultimate elongation) |
501 | 503 | 508 | 528 | 325 | 420 | 469 |
| 反発弾性(%) (rebound resilience) |
70 | 69 | 70 | 71 | 61 | 68 | 70 |
| 銘柄(description) | アサヒ サーマル |
AX-015 | IRB 7 |
|---|---|---|---|
| 試験項目(test items) | |||
| ムーニー粘度 (mooney viscosity) '@125℃ ML1+4' |
50 | 72 | 62 |
| ムーニースコーチ (mooney scorch) '@125℃ t5 |
11.6 | 9.9 | 9.2 |
| 硬さ (hardness) (JIS) |
61 | 72 | 70 |
| 300%モジュラス(MPa) (300%modulus) |
11.6 | 16.7 | 18.7 |
| 引張強さ(MPa) (tensile strength) |
22.9 | 24.3 | 27.0 |
| 伸び(%) (ultimate elongation) |
510 | 356 | 420 |
| 反発弾性(%) (rebound resilience) |
67 | 48 | 57 |
- ※加硫時間は30分です。
- ※但し、アサヒサーマル、旭#15、旭#15HS配合部数は75部です。
NR配合表
| NR | 100 |
|---|---|
| カーボンブラック | 50 |
| ステアリン酸 | 3 |
| 亜鉛華 | 5 |
| 促進剤DM | 0.6 |
| 硫黄 | 2.5 |